Welding technology of digger gp bucket and bucket teeth

Good quality Heavy Duty Excavator Bucket for sales
We tried our first order in 2018, which was two years after I exchange my business card with Alice in 2016 Bauma conexpo India. Our supplier didn't finish our order on time, and it will cause around 100,000 USD lose to us. That's when we tried Huitong the first time. Huitong is good at dealing with rush orders, and the quality is very good.

—— Mr.Varun, Dealer, India

I work with Huitong the first time when I started my importing business. I've got tons of market insights from Jeremy. He is such a good friend being very tolerant to my bad temper. In 2017, Jeremy helped me handle a problem of bill of lading, which is caused by me. Huitong always emphasize that we should deal with the problem as soon as it occurs.

—— Mr.Stanislav Lilov, Bulgaria

We started cooperated with Huitong from 2017, they are honest, professional, always help us slove problems at the first step, we buy excavator attachments from Huitong in one stop, we share market insights like a good friend. Love Their Work.

—— Sony

I'm Online Chat Now
Company News
Welding technology of digger gp bucket and bucket teeth
Welding technology of digger gp bucket and bucket teeth

1. Preparation before welding

First cut off the worn bucket teeth from the digger gp bucket body, and then use an angle grinder to polish the place where the bucket teeth are installed. There should be no dirt, rust, and check carefully for cracks and other defects; use carbon arc on the bucket teeth to be welded Gouging out the groove and clean it with an angle grinder.

 

digger gp bucket

 

2. Welding

①First, use GBE309-15 electrode for surfacing welding on the bucket body (joint with bucket teeth). The electrode must be dried at 350℃ for 15h before welding. The welding current should be too large and the welding speed should be slightly slower to ensure the fusion zone. The nickel content is 5% to 6% to prevent the generation of martensite sensitive to cracks.

 

② Perform tack welding. After the bucket teeth are assembled in place, use a D266 electrode with a diameter of 32MM to perform two-sided symmetrical tack welding, and the length of the weld should not exceed 30MM. Water cooling and hammering immediately after welding.

 

③ Bottom welding. Use D266 electrode with a diameter of 32MM for bottom welding. Use small current, DC reverse polarity, intermittent welding, short section welding. Water cooling should be done in time every time welding is stopped, and the temperature of the interlayer should be controlled below 50℃.

 

④ Perform filler welding. After the bottom welding is completed, use D266 electrode with a diameter of 4MM for intermittent welding. The welding current is 160A. One electrode is divided into 3 to 4 times to complete the welding. When the welding is stopped, the welding bead must be cooled to 50℃ with water in time. Below, hammering is performed to eliminate stress and prevent carbide precipitation; each two layers are welded, the left and right welds are alternately welded to ensure the symmetry of the welding, until the weld foot reaches 16MM. Use a magnifying glass to check the cracks after each weld. If there are cracks, use carbon arc gouging to eliminate them before welding.

 

digger gp bucket

 

After the digger gp bucket body and bucket teeth were welded and repaired, after more than a year of use, the welds were still good. This method has high efficiency, low cost and good effect in repairing bucket teeth, and has certain practical value.